'性表性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTM D638/ISO 527470
（46）kg/cm²(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 527--%拉伸模量 ASTM D638/ISO 527--kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 527--%拉伸断裂伸长率(延伸率) ASTM D638/ISO 527--%弯曲模量(弯曲弹性率) ASTM D790/ISO 17828000（2750）kg/cm²(MPa)[Lb/in2]弯曲强度 ASTM D790/ISO 178840
（83）kg/cm²(MPa)[Lb/in2]洛氏硬度 ASTM D785R-108 IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 17920（196）kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.05 成型收缩率 ASTM D9550.4-0.7%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 11331.7g/10min220℃/10kgASTM D1238/ISO 113319g/10min吸水率 23℃/24H ASTM D570/ISO 62--%热性能热变形温度退火ASTM D648/ISO 7589℃（℉）未退火ASTM D648/ISO 75101℃（℉）维卡软化点 ASTM D1525/ISO R306104℃（℉）熔点 ---℃（℉）燃烧性（率） UL94HB 线性膨胀系数 ASTM D696/ISO 11359--mm/mm.℃加工条件干燥条件    加工温度射嘴  ℃料筒前段  ℃料筒中段  ℃料筒后段  ℃熔体温度   ℃模具温度   ℃压力注塑压力  Mpa保压压力  Mpa背压  Mpa螺杆转速   rpm其他备注--颜色米黄特性高光泽、中冲击性、高温成型性。适用于：玩具、时钟外壳、音响外壳、手提箱、家电外壳等用途性表数据提供企业[ 深圳华宇创业 ] | 数据修正企业[ 暂无! ]性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTM D638/ISO 527470
（46）kg/cm²(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 527--%拉伸模量 ASTM D638/ISO 527--kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 527--%拉伸断裂伸长率(延伸率) ASTM D638/ISO 527--%弯曲模量(弯曲弹性率) ASTM D790/ISO 17828000（2750）kg/cm²(MPa)[Lb/in2]弯曲强度 ASTM D790/ISO 178840
（83）kg/cm²(MPa)[Lb/in2]洛氏硬度 ASTM D785R-108 IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 17920（196）kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179--kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.05 成型收缩率 ASTM D9550.4-0.7%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 11331.7g/10min220℃/10kgASTM D1238/ISO 113319g/10min吸水率 23℃/24H ASTM D570/ISO 62--%热性能热变形温度退火ASTM D648/ISO 7589℃（℉）未退火ASTM D648/ISO 75101℃（℉）维卡软化点 ASTM D1525/ISO R306104℃（℉）熔点 ---℃（℉）燃烧性（率） UL94HB 线性膨胀系数 ASTM D696/ISO 11359--mm/mm.℃加工条件干燥条件    加工温度射嘴  ℃料筒前段  ℃料筒中段  ℃料筒后段  ℃熔体温度   ℃模具温度   ℃压力注塑压力  Mpa保压压力  Mpa背压  Mpa螺杆转速   rpm其他备注--颜色米黄特性高光泽、中冲击性、高温成型性。适用于：玩具、时钟外壳、音响外壳、手提箱、家电外壳等用途'