Physical PropertiesMetricEnglishComments![](http://asia.matweb.com/images/spacer.gif)
Density1.37 0.0495 lb/in? ISO 1183Specific Gravity1.37 0.0495 lb/in? Method A; ASTM D792Water Absorption0 %0 % at 24 hrs; ASTM D570Linear Mold Shrinkage0.013 cm/cm0.013 in/in ASTM D955Linear Mold Shrinkage, Transverse0.019 cm/cm0.019 in/in ASTM D955
Mechanical PropertiesTensile Strength at Break69.6 MPa10100 psi ASTM D638Tensile Strength, Yield74.5 MPa10800 psi ASTM D638Elongation at Break23 %23 % ASTM D638Elongation at Yield5.8 %5.8 % ASTM D638Tensile Modulus2.9 GPa421 ksi ASTM D638Flexural Modulus2.96 GPa429 ksi ASTM D790Flexural Strength117 MPa17000 psi ASTM D790Izod Impact, Notched0.961 J/cm1.8 ft-lb/in 3.18 mm; ASTM D256Izod Impact, Notched (ISO)8.8 kJ/m?4.19 ft-lb/in? ISO 180Izod Impact, Unnotched15.5 J/cm29 ft-lb/in 3.18 mm; ASTM D256Izod Impact, Unnotched (ISO)91.2 kJ/m?43.4 ft-lb/in? ISO 180Falling Dart Impact2.8 J2.07 ft-lb ASTM D3763Impact Test1.35 J0.996 ft-lb Multi-Axial Instrumented Impact Energy; ISO 6603-2Coefficient of Friction0.520.52 vs. Steel - Dynamic @ 40 psi, 50 ft/min, tested in ordance with LNP WI-0687; ASTM D1894Coefficient of Friction, Static0.430.43 vs. Steel @ 40 psi, tested in ordance with LNP WI-0687; ASTM D1894K (wear) Factor258 x 10-8mm?/N-M128 x 10-10in?-min/ft-lb-hr 40psi, 50ft/min; tested in ordance with LNP WI-0687
Processing Properties